20-roll rolling mill, also known as a cluster mill, offers several advantages in titanium strip production compared to traditional rolling mills. Here are some of the advantages:
Improved Thickness Control: The 20-roll rolling mill provides enhanced control over the thickness of the titanium strip. The large number of rolls allows for more precise adjustments and reduces thickness variations across the strip. This results in a more uniform and consistent product with tighter tolerances.
Better Surface Finish: The multiple rolls in a 20-roll mill allow for improved surface finish of the titanium strip. The increased number of contact points between the rolls and the strip helps to smooth out any surface imperfections and reduce the occurrence of defects such as scratches or marks.
Increased Productivity: The 20-roll rolling mill offers higher production rates compared to traditional mills. The multiple rolls allow for higher rolling speeds and increased throughput, resulting in greater productivity and efficiency in titanium strip production.
Enhanced Shape Control: The cluster mill design of a 20-roll rolling mill provides better shape control of the titanium strip. The rolls can be individually adjusted to achieve the desired strip shape, such as flatness or crown control. This helps to ensure that the titanium strip meets the required dimensional specifications.
Reduced Edge Cracking: Titanium is a challenging material to roll due to its low ductility and high strength. The 20-roll rolling mill's design helps to minimize edge cracking during the rolling process. The multiple rolls distribute the rolling forces more evenly, reducing stress concentrations at the strip edges and minimizing the risk of cracking.
Improved Material Utilization: The precise control and uniformity provided by a 20-roll rolling mill contribute to better material utilization. With tighter thickness tolerances and improved shape control, there is less material waste due to out-of-specification products. This leads to cost savings and improved overall efficiency.
It's important to note that the specific advantages of a 20-roll rolling mill in titanium strip production may vary depending on the specific design, configuration, and process parameters of the mill. Manufacturers and operators of the rolling mill can further optimize the process to maximize the benefits and address specific challenges associated with titanium strip production.
| Name | Titanium Strip andFoil,Tape | Dlivery Status |
| According to your requirements or sheet Hot rolling cold rolling coil rolling-annealing cold rolling-annealing smooth according to your Hardness Requirements | ||
| Standard | GB/T3621.ASTM B265 | |
| Certification | IOS9001:2015,ISO/TS 16949:2009 | |
| Wall thickness | 0.08-3.0mm | |
| Allowable width Deviation | +/-0.15 mm | |
| Material | Gr1(TA1),Gr2(TA2),Gr12(TA10) | |
| Delivery time | Within 25 days after receiving deposit | |
| Payment term | T/T,L/C | |
| Supply ability | 250 tons per month | |
| Packing | Export standard package with polywood pallet or ISPM 15 stamped wooden case | |
| Information | Max coil weight:10000KG Coil inner Diameter Φ500/600/610/762 The Narrowest slitting slip width:15mm Max Length:5600M |
牌号 Grade | 厚度 Thickness（mm） | 厚度允许偏差 Allowable Thickness Deviation(mm) | 材料宽度 Width（mm） | 允许宽度偏差 Allowable width Deviation(mm) | |
普通精度 General precision | 高精度 High Precision | ||||
TA1/GR1 TA4/GR4 TA2/GR2 TC4/GR5 TA10/GR12 | 0.01<T≤0.1 | +/-0.01 | +/-0.005 | 5～1200 | +/-0.1 |
0.1<T≤0.6 | +/-0.01 | +/-0.005 | |||
0.6<T≤1.0 | +/-0.01 | +/-0.005 | |||
+/-0.02 | +/-0.01 | ||||
1.0<T≤2.0 | |||||
牌号 Grade | 状态 Status | 室温力学性能 Room-Temperature Mechanical Properties | |||
抗拉强度Rm/Mpa Tensile Strength Rm/Mpa | 规定非比例延伸强度Rp0.2/Mpa Provisions of Non-proportional Extension Intensity Rp0.2/Mpa | 断后伸长率A50 mm/% Precentage Elongation after Fracture | |||
TA1/GR1 | 退火态 Annealed | ≥240 | 140～310 | ≥24% | |
TA2/GR2 | ≥400 | 275～450 | ≥20% | ||
TA10/GR12 | ≥460 | ≥300 | ≥18% | ||